Pó magnético macio FeSiCr para estrangulamento de moldagem
Ferrosilicon powder is made by melting a fixed ratio of high purity iron and crude ferrosilicon in an induction furnace. The molten metal is then atomised using a high pressure stream of nitrogen gas to produce a high-grade ferrosilicon powder.
Because of its excellent DC bias and extremely low core loss, the gas atomized soft magnetic alloy powder is widely used in the manufacture of high performance magnetic powder core and large current molding choke.
Descrição
Ferrosilicon powder is made by melting a fixed ratio of high purity iron and crude ferrosilicon in an induction furnace. The molten metal is then atomised using a high pressure stream of nitrogen gas to produce a high-grade ferrosilicon powder.
Because of its excellent DC bias and extremely low core loss, the gas atomized soft magnetic alloy powder is widely used in the manufacture of high performance magnetic powder core and large current molding choke.
Informações Gerais
| Lugar de origem: | Changsha, China |
| marca: | HLPOWDER |
| Item: | FeSiCr |
| Tamanho das partículas: | D50: 11μm/9μm /6μm |
| Certificação: | ISO9001, ISO14001 |
| Quantidade mínima: | 20kg |
| Detalhes da embalagem: | Barril de ferro |
| Tempo de entrega: | dias 7-10 |
Aplicações
● Computador
● Comunicação
● Eletrônicos de Consumo:
● Automotiva
● Eletrônicos médicos
Especificações
Composição química:
| Liga | Cr | Si | S | P | C | O |
| FeSiCr | 4.2-4.8 | 6.2-6.8 | ≤ 0.01 | ≤ 0.02 | ≤ 0.03 | ≤0.04 or ≤0.06 |
| FeSiCr | 4.2-4.8 | 3.4-4.0 | ≤ 0.01 | ≤ 0.02 | ≤ 0.03 | ≤0.04 or ≤0.06 |
Tamanho da partícula:
D50:11/9/6um
Características do pó
● Maior densidade de indução de saturação
● Características de polarização CC mais elevadas
● Menor perda de núcleo
● Melhor estabilidade de temperatura
● Melhor resistência à corrosão
Pacote
Para moldagem de estranguladores: Cada embalagem de PE + tambor de ferro de 25 kg/50 kg ou big bag de 500 kg/1000 kg.